Item

Unit

Value

Test Standard

Thickness

um

50±5

ASTM D374

Color

/

Translucent

Visual

UV Curing Parameter

365nm @70mW for 60 secs

SG Method

Open time after UV*

Hours

8

SG Method

Final bonding time (at RT)

Hours

48

SG Method

Final bonding time (at 70C)

Hours

3

SG Method

Glass transition temperature (after UV curing)

oC

66

DMA

180o Peel adhesion strength (SUS)

Before UV curing

N/inch

13

ASTM D3330

After UV curing

33

Dynamic shear strength

(SUS/SUS)

MPa

>15

ASTM D1002

Modulus (at ~23C)

Before UV curing

MPa

0.12

DMA

After UV curing

MPa

1478

DMA